ISO 15912:2016 pdf free
ISO 15912:2016 pdf free.Dentistry一Refractory investment and die material
powdered particulate refractory and binder system that is mixed with a specified liquid to produce a pourable fluid that sets around a pattern to form the mould for casting a dental metallic prosthesis
Note 1 to entry: In some products, the binder may be dispersed in the refractory powder and the product is supplied as a mixed powder. Alternatively, the chemistry of the binder may lead to it being present in a solution (to be used with the powder that is supplied) with part or none of it being dispersed in the refractory powder, as received.
Note 2 to entry: The specified liquid may be pure water, an aqueous binder solution, or an aqueous solution to enhance expansion.
powdered particulate refractory and binder system that is mixed with a specified liquid to produce a fluid that sets (and is designed specifically) to form of a hard die, suitable for the production of a dental ceramic prosthesis using the sintering technique
powdered particulate refractory and binder system that is mixed with a specified liquid to produce a fluid that sets (and is designed specifically) to form a cast upon which metallic components are held, or are partly embedded, accurately in place while they are joined by brazing
Note 1 to entry: The cast may be referred to as the model, though that is a deprecated term.
powdered particulate refractory and binder system that is mixed with a specified liquid to produce a pourable fluid that sets around a pattern to form a mould into which a dental pressable-ceramic,softened by heating, can be forced under pressure
heating method in which (at a time after setting that is recommended by the manufacturer) the dental casting investment mould, or dental pressable-ceramic mould, or dental brazing investment cast or dental refractory die is placed in a burn-out furnace set at room temperature, after which the temperature of the furnace is increased to the end temperature in a series of stages and at a programmed rate recommended by the manufacturer
heating method in which (at a time after setting that is recommended by the manufacturer) the dental casting investment mould, or dental pressable-ceramic mould, or dental brazing investment cast, or dental refractory die is placed directly into the hot burn-out furnace that is set and held at the burn-out temperature recommended by the manufacturer.ISO 15912 pdf free download.